Ročno - pihano steklo ni le ena najpogostejših, ampak tudi najstarejše metode pri izdelavi stekla . Ste se kdaj spraševali, kako se ti osupljivi, odlično izdelani koščki steklene posode končajo na ogled? Katera orodja so vključena v ta zapleteni postopek? Vzemimo se globoko potapljanje v očarljiv svet roke - pihano steklo in izvemo!

The basic steps of hand - blown glass forming include creating a small bubble, a large bubble, blowing to shape, final shaping, and pre - furnace hot working. Pre - furnace hot working covers operations like cutting the edge, expanding the mouth, and refining the shape. The process varies depending on the shape of the glass product. Glass products can be categorized into "Burst - usta" in "odprta - usta", ki temeljijo na proizvodnem procesu .

For burst - mouth products, the excess part of the glass cap is trimmed during the cold - working stage. As for open - mouth products, after being removed from the mold, another craftsman uses a separate blowing pipe to pick up a small amount of molten glass and attach it to the bottom of the glass product, a process called "topping with the pump." At the same time, the seam at the mouth of the mold is broken, and the product is repeatedly heated for pre - furnace hot working. After annealing in the kiln, the bottom of the product undergoes grinding and polishing during the cold - working stage. The most obvious difference between the two types is that open - mouth products have marks from the topping process at the bottom, while burst - mouth products show signs of grinding around the usta .

Potrebna oprema in orodja

1. pihanje cevi

Blowing pipes used in glassblowing are made from iron, stainless steel, or nickel - chromium alloy. Iron pipes can contaminate the molten glass with iron when in contact with it. However, since iron pipes are the most affordable, in large - scale industrial production, a section of stainless steel or nickel - chromium alloy is often welded to the front end of the železna cev . Sprednji konec pihalne cevi je lahko ravna ali ima večji material - nabiranje površine, zadnji del pa ima vedno ukrivljeno površino .
Cev z ravnim sprednjim koncem lahko v prvem potopitvi pobere več steklenega materiala, kar omogoča, da se korak pihanja začetnega majhnega mehurčka preskoči . Ta vrsta je idealna za postopek uporabe steklene palice za prekrivanje materiala ., saj je ustnik za pihanje zraka, ki se je vgradila z gladko cevjo ali lesečico, ki je vgrajena z gumijasto cevjo ali leseči vrtenje . Če želite pritrditi gumijasto cev, se pihala cev najprej segreje, dokler ne sveti rdeče - vroče . Nato se gumijasta cev hitro zdrsne na cev, medtem ko je vroča . guma mehčala in zlahka ustreza cevi {{6}, ki jo enkrat ohladi.

2. mehurček - hladilni stroji

Bubble - Hladilni stroji poganjajo majhni električni motorji . Uporabljajo verige in druge komponente za vrtenje krožnega diska, pri čemer se pihalne cevi nenehno vrtijo . To zagotavlja, da stekleni mehurčki ohranijo okrogle oblike ., ki lahko z enim obdelovalnim pihanjem, ki ga lahko obvladuje, da je eno samo obvladovanje, ki ga je mogoče eno samo obvladovati, enotni obrti, ki lahko obvladujejo multimegim, ki ga lahko sam obvladuje večkratno pihanje, z enim obdelovanjem, ki ga lahko sam obvladuje večkratni pihal. Oblikovanje mehurčkov jih prevzame drug obrtnik . en sam mehurček - hladilni stroj lahko hkrati hrani dve ali več pihalnih cevi .

3. Rolling Bowls

Kotalne sklede so polkrožne, votle železne strukture, ki jih podpirajo litini - železni okvirji . voda teče skozi gumijasto cev, da ohladi sklede ., potem ko obrtnik razstreli majhen mehurček in pobere več steklenega materiala, medtem ko pihajo v okrog, ki se nahajajo v krog . shaping. To prevent the glass from cooling too quickly and to add lubrication, multiple layers of newspaper or cardboard are lined inside the iron rolling bowl. When the red - hot glass touches the paper, it carbonizes, creating a layer of carbonized gas that acts as a lubricant between the glass and the bowl. Many foreign artists prefer wooden rolling Podejane . Lesene sklede so majhne, ​​lahke in enostavne za držanje, zaradi česar je oblikovanje kozarca bolj priročno ., ko stekleni mehurček pride v stik z lesom, je manj verjetno, da pustijo oznake plesni ali hladne pike .

4. pečice

Pečice se uporabljajo za ogrevanje stekla, zlasti okoli območja ust . deljene pečice so ponavadi v visokem temperaturnem stanju in so običajno enotne pečice, ki se nahajajo v bližini peči ., to so preproste pečice, ki segrejejo s plinom ali gorivom, ki lahko dosežejo temperature med 1100 - 1200 stopinja Delo . V dejanski proizvodnji je pečica v uporabi le približno 50% celotnega časa proizvodnje .
Ko se hkrati uporablja več odprtin pečice, je ključnega pomena, da notranjost ohrani pri konsistentni visoki temperaturi ., vendar zaradi velikega notranjega prostora te pečice porabijo veliko energije . z uporabo malenoidnih ventilov za nadzor nad stojalo, ko je razvida, da je OVE PREDSTAVLJA solenoid valve opens, ensuring the proper ratio of air and gas for heating. When the blowing pipe is removed from the stand, the solenoid valve closes, reducing the air and gas flow and lowering the temperature, which saves a lot of energy. These ovens are mainly used for processing the mouth of the glass products, and in some factories, they're simply called "mouth - heating pečice . "

5. Druga bistvena orodja

Potrebnih je več drugih orodij, kot so lopate, klešče, pincete, sponke, škarje in padle . Škarje se uporabljajo za obrezovanje ust kozarca med pihanjem, klešče za širitev ust in vilice za postavitev izdelkov v žarjenje v žaronjenje peči .

Postopek oblikovanja stekla za roke

1. zbiranje stekla

Obrtnica potaplje pihalno cev v lonček, napolnjen z staljenim steklom . Po pregrevanju se cev vstavi pod kotom 45 - 50 stopinj v molljeno steklo, ki doseže globino {{2} {3}. .. ... Steklo . Po tem se cev obrne na levo - spredaj, da razbije stekleno nit in odstrani . Zbrano steklo se nato oblikuje v okroglo maso . Za isto vrsto stekla je teža, ki je bila pobrana, postavljena na drobno, ki je na zbranem, da se s steklom, ki se zbira, na zbrano plošča vrti .

2. piha majhen mehurček

After the gathered glass cools slightly (you can tell by the change in color), the craftsman blows air into it to form a small bubble. For larger glass artworks, the small bubble is used to pick up more glass material one or more times. After re - gathering the glass, a metal rolling plate or rolling bowl is often used to roll the glass, giving it a symmetrical shape and a smooth Surface . Zunanji premer majhnega mehurčka je običajno 2/5 do 4/5 premera odprtine kalupa . Majhen mehurček mora biti enakomerno debel in brez umetnih zračnih mehurčkov .

3. Ustvarjanje velikega mehurčka

Majhen mehurček se znova uporablja za zbiranje več steklenega materiala . Vstavljen je približno 2/3 v staljeno steklo in se vrti tako, da steklo enakomerno pokriva majhen mehurček . Ko poberem material, mora obrtnik, ki stalno stopi, obrniti cev in ga potisniti naprej, da bi ga prelomil, da bo steklo spredaj razbil steklo, da bi spredaj spredaj razbil steklo, da bi se v koraku spredaj spredaj spredaj razbil steklo spredaj, ko ste se spredaj lotil stekla, da bi se v koraku spredaj spredaj razbil steklo spredaj, ko ste se spredaj lotil stekla, ki je na levi strani, da bi se spredaj lotil stekla, da bi se steklo spredaj lotilo stekla spredaj, ko ste steklo spredaj, spredaj spredaj, spredaj spredaj, da bi steklo spredaj razbile, da je steklo spredaj spredaj spredaj, ki je v koraku spredaj spredaj, spredaj spredaj v koraku. Ohlajen in oblikovan je v valjani posodi, ki mora imeti pravilno količino vode . med delovanjem, sprednja roka mora biti nižja od zadnje roke, cev pa je treba hitro, nežno in vztrajno, da se debelina stekla enakomerne ., nato pa se pretrese, da se zrak zasuka, medtem ko jo pretreseta, da bi se zmanjšala temperatura in zunaj {7 {7 {7. Hitrost in smeri pihalne cevi lahko steno mehurčkov naredimo enakomerno simetrično ., ki postavljanje mehurčka navpično navzgor naredi dno debelejše, in zamah po cevi navpično navzdol raztegne mehurček . končno bi moral velik mehurček približati obliki molla in biti {{10}% BE {{10}% BE {{10}% BE {{10}% BE {{10}

4. pihanje in oblikovanje v kalupu

The large bubble is placed into the mold. For rotating - blown products, the blowing pipe needs to be continuously rotated while blowing, while for static - blown products, air can be blown directly. This causes the bubble to expand and fill the entire mold cavity, taking on the desired shape. At the beginning, the blowing should be slow, and the air should be Nežno uvedene . tako kovinske kot lesene kalupe je treba ohladiti z vodo . kovinske kalupe so obložene z ogljikovo prevleko (znano tudi kot "saja"), leseni kalupi pa so obloženi s časopisom ., ko je izdelka mogoče, je mogoče odstraniti iz modela, ki se lahko izdelan od masaž - Izdelani stekleni izdelki .
Ko umetniki ustvarjajo, saj ponavadi naredijo manj kosov in si prizadevajo za edinstvene umetniške učinke, pogosto uporabljajo vsakdanje predmete različnih materialov kot kalupi . na primer nekateri umetniki zložijo votle opeke, ki jih uporabljajo kot plesni, kar daje izdelku teksturirano, neenakomerno površino .